Oneflex Hose
Brand :ZYfire
Product origin :China
Delivery time :15days
Supply capacity :500,000mtr. per month
Oneflex Premium
Through-the-weave NBR frac water hose
Lining Properties:
a. Ultimate Tensile Strength: Tensile strength of the lining and cover shall not be less than 1500psi (10,500kpa);
b. Ultimate Elongation: 400% minimum;
c. Accelerated Ageing Test.
Tube and cover: Nitrile/TPR Blend, ribbed cover for maximum abrasion resistance. Thick wall.
Reinforcement: 100% virgin high tenacity polyester Jacket.
Application: Water discharge, Transfers, Drainage, Irrigation installations, Pumping of sludge and liquid fertilizers, Chemical industry, Refineries, Air pressure Premium Solution.
Temperature: -25℃ to +100℃ （-13℉ to 212℉）
Standard length: 15m (50ft), 20m (66ft), 30m (100ft), 60m (200ft), 90m (300ft), 200m (660ft), 300m (990ft)
Color: Red, Yellow, Orange, Blue, Black
| ID | Tolerance | Wall Thickness | Service Pressure | Min Burst Pressure | Weight | |||
| inch | mm | mm | inch | mm | psi | psi | lbs/ft | kg/m |
| 3" | 76 | 76-78 | 0.118 | 3.00 | 200 | 600 | 0.67 | 1.00 |
| 4" | 102 | 102-104 | 0.126 | 3.20 | 200 | 600 | 0.94 | 1.40 |
| 6" | 152 | 154-157 | 0.126 | 3.20 | 200 | 600 | 1.47 | 2.20 |
| 6" | 152 | 154-157 | 0.138 | 3.50 | 250 | 750 | 1.68 | 2.50 |
| 6" | 152 | 154-157 | 0.165 | 4.20 | 300 | 900 | 1.88 | 2.80 |
| 8" | 204 | 204-207 | 0.157 | 4.00 | 200 | 600 | 2.41 | 3.60 |
| 8" | 204 | 204-207 | 0.165 | 4.20 | 300 | 900 | 2.55 | 3.80 |
| 8" | 204 | 204-207 | 0.197 | 5.00 | 400 | 1200 | 2.75 | 4.10 |
| 10" | 254 | 254-257 | 0.173 | 4.40 | 200 | 600 | 3.10 | 4.63 |
| 10" | 254 | 254-257 | 0.177 | 4.50 | 300 | 900 | 3.35 | 5.00 |
| 12" | 306 | 306-311 | 0.157 | 4.00 | 150 | 450 | 3.35 | 5.00 |
| 12" | 306 | 306-311 | 0.177 | 4.50 | 200 | 600 | 4.02 | 6.00 |
| 14" | 356 | 356-360 | 0.189 | 4.80 | 150 | 450 | 4.96 | 7.40 |
| 16" | 400 | 406-411 | 0.181 | 4.60 | 100 | 300 | 5.13 | 7.65 |
*All above technical parameters are for reference, details please confirm with ZYfire.
The tensile strength and ultimate elongation of the vulcanized rubber compound which has been subjected to the action of oxygen at a pressure of 300psi +/-10psi, (2100kpa+/-70kpa) and temperature of 70 degrees centigrade +/- degree centigrade (158 F +/- 18F) for a period of 96 hours shall be greater than 60% of the original properties stated.